ASTM: 310S, BS EN: 1. 4845
Characteristic: Suitable for making all kinds of furnace components, the highest temperature is 1300 C, and the continuous use temperature is 1150 C. 310S is a standard method for stainless steel in the United States. Its domestic label is (2520) 0Cr25Ni20. It is an austenitic stainless steel. S in 310S refers to the special use of this stainless steel. 0Cr25Ni20 (310S) characteristics – high temperature oxidation resistance, high temperature strength. Usage – Exhaust Bellows, Microwave Heater, Tube, High Temperature Furnace Gallbladder, Cremation Furnace and other steel grades requiring heat resistance, high temperature/high temperature contact parts.
310S:25Cr-20Ni series high alloy stainless steel has excellent oxidation resistance at high temperature and is suitable for heat-resistant parts below 1000 C.
|
Steel grade |
–SUS310S |
|
Characteristic |
–high temperature oxidation resistance, high temperature strength |
|
Usage |
–Steel grades requiring heat resistance such as exhaust pipe Bellows, microwave oven Heater, Tube, cremation furnace, high heat/high temperature contact parts (below 1000 C) |
Chemical Constituents: (Unit: wt%)
|
Specification |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
OTHER |
|
TYPE |
≤0.08 |
≤1.50 |
≤2.00 |
≤0.045 |
≤0.030 |
24.0～26.0 |
19.0～22.0 |
- |
Mechanical properties:
|
YS（Mpa） |
YS（Mpa） |
TS（Mpa） |
EL（%） |
Hv |
|
TYPE |
≥205 |
≥520 |
≥40 |
≤200 |
Physical properties:
|
density (g/cm3) |
(g/cm3) magnetic specific heat |
Thermal Conductivity 250C(J/g.0C) |
Thermal Expansion Rate 1000C(W/m) |
20~1000C(10-6/0C) |
|
7.98 |
无 |
0.50 |
14.2 |
15.9 |
Mechanical properties:
Hardness (HB): <187
Tensile Strength (b) (Mpa): > 520
Yield Strength (_s) (Mpa): > 205
Elongation (delta)%: > 40
Area reduction (_)%: > 50
heat treatment
Melting point: 1400 ~ 14500C;
Solution treatment: 1030 ~ 11800C.